BALORA PVD MCrAlY
BALORA PVD MCrAlY

In order to improve the efficiency level of gas turbines, the operating temperatures are often increased to 1,200 °C and above. The coatings used in the hot section must withstand these extreme conditions to prevent hot corrosion and component oxidation, otherwise a system failure would occur – resulting in considerable replacement costs.

Typically, MCrAlY coatings are produced using thermal spraying and other technologies. Oerlikon Balzers has applied its proven high-end PVD Arc technology to make the standard MCrAlY coating production process more efficient and significantly improve the coating properties.

BALORA™ PVD MCrAlY offers superior properties compared to conventionally produced MCrAlY coatings: it has excellent substrate adhesion, and it can be applied up to a thickness of 100 micrometres without porosity. Most importantly, the MCrAlY composition in combination with the high density can be tailored to form the perfect barrier against oxidation on turbine blades and vanes.

BALORA PVD MCrAlY
Matériau de revêtement NiCrAlY (Ni, Ni/Co, Co)
Technologie de revêtement Arc
Couleur du revêtement grey
Dureté du revêtement HIT [GPa].* 7 - 11
Temp. de service max. [°C]**** 1200
Température du procédé [°C] 400 - 500
Épaisseur de couche typique [µm] 0.1 to > 100
Remarque générale Toutes les valeurs spécifiées sont approximatives et dépendent de l'application, de l'environnement et des conditions d'essai.
*Dureté du revêtement HIT [GPa]. Mesuré par nanoindentation selon ISO 14577. Pour les revêtements multicouches, la dureté de chaque couche varie.
****Temp. de service max. [°C] Il s'agit de valeurs approximatives issues de la pratique. Les lois thermodynamiques induisent une dépendance de pression dans l'application.