BALINIT CROMA / CROMA PLUS With BALINIT CROMA, your plastics processing will be in top form even for large components.

BALINIT CROMA / CROMA PLUS

Whether injection moulding, extrusion or blow moulding - only top quality surfaces ensure optimal manufacturing productivity and efficiency. BALINIT® CROMA and BALINIT® CROMA PLUS are thus the best choices for successful plastics processing, even for large components.

CROMA and CROMA PLUS reduce tool, production and maintenance costs, making them the ideal coatings for PVC window frame and plastic extrusion, and for rubber processing.

  • Extreme coating hardness
  • Low coefficient of friction
  • Excellent adhesion
  • Increased productivity, economic efficiency  and reliability
  • Coating of large components
 
 
 
BALINIT CROMA
Coating material CrN
Coating technology Arc
Coating colour silver-grey
Coating hardness HIT [GPa]* 25+/-3
Coefficient of friction (dry) vs. steel** ~0.5
Max. service temp. [°C]**** 700
Process temperature [°C] 500
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.
BALINIT CROMA PLUS
Coating material CrN + OX
Coating technology Arc
Coating colour rainbow
Coating hardness HIT [GPa]* 25+/-3
Coefficient of friction (dry) vs. steel** ~0.5
Max. service temp. [°C]**** 700
Process temperature [°C] 500
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.