BALDIA NANO High-performance machining of fibre-reinforced composites, stack materials and Al alloys

BALDIA NANO
BALDIA NANO
BALDIA NANO
BALDIA NANO

Tools coated with BALDIA® NANO can reliably machine fibre-reinforced composites (GFRP, CFRP), stack materials and Al alloys (Si>12%).

Selecting the ideal interface engineering prevents burr formation and delamination. Tight tolerances can be achieved for the coating thickness or the tool diameter.

Longer tool life and better surface quality significantly reduce manufacturing costs.

Note: BALDIA NANO was previously named BALINIT DIAMOND NANO.

BALDIA NANO
Coating material C-based (sp3)
Coating technology CVD
Coating colour grey
Coating hardness HIT [GPa]* 80 - 100
Max. service temp. [°C]**** 600
Process temperature [°C] < 900
Typical coating thickness [µm] 6 - 12
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.