BALINIT PROTECREACH compliant coatings for enhanced protection on industrial gas turbine compressors

BALINIT PROTEC for enhanced protection on industrial gas turbine compressors
BALINIT PROTEC for industrial gas turbine blades

Solid Particle Erosion (SPE), Liquid Droplet Erosion (LDE) and corrosion of turbine blades are three key defects that significantly influence the performance of gas turbine compressors. This should not be underestimated as the resulting decrease in efficiency will cause an increase in cost for your plant.

BALINIT® PROTEC by Oerlikon Balzers is a REACH-compliant coating especially developed to protect industrial gas turbine compressors from corrosion and erosion. Moreover, this new PVD coating can substantially improve the efficiency of compressors.

As a leading global supplier of surface solutions with almost 75 years of experience, based on a strong R&D department, we at Oerlikon Balzers understand the needs of our customers. This has always been our motivation to passionately develop the right PVD coating solution in close partnership - perfectly tailored to your needs.

  • Преимущества


    EU REACH compliant
    BALINIT® PROTEC does not use the toxic and hazardous hexavalent Cr-VI
    Reduction of cavitation from Water Droplet Erosion (WDE) caused by fogging and wet compression systems
    Increased asset life and compressor protection
    Enhanced protection from Solid Particle Erosion (SPE)
    Outperforms the current industry standard galvanic sacrificial coatings
    Superior surface finish
    Improved efficiency with standard surface smoothness of Ra < 0.8 µm
    Surface finish can be further enhanced by post polishing
    Increased corrosion protection on gas turbine compressors
    Has passed the ASTM B117 salt fog and OEM sulphur tests

    Advanced REACH compliant protection with a NEW PVD corrosion resistant coating

  • Спецификации


    Материал покрытия AlN-based
    Структура покрытия Arc
    Цвет покрытия grey
    Твердость покрытия HIT (ГПа)* 20 +/- 1
    Макс. рабочая темп. [°C]**** 1200
    Температура нанесения покрытия [°C] < 500
    Типичная толщина покрытия [мкм] 5 - 25
    Общее примечание Все приведенные данные являются приблизительными, они зависят от применения, окружающих условий и условий испытания.
    *Твердость покрытия HIT (ГПа) Измерено посредством наноиндентирования согласно ISO 14577. Твердость разных слоев многослойных покрытий отличается.
    ****Макс. рабочая темп. [°C] Это приблизительные значения, полученные не в практических условиях. В соответствии с законами термодинамики имеется зависимость давления в конкретном случае применения.