BALINIT CNI is a very smooth sputtered Chromium Nitride (CrN) coating. It is very ductile and has a high oxidation resistance. It is the coating which can be produced in highest thicknesses (up to 50 µm). Mainly used for high temperature sliding applications like engine exhaust valves and piston rings. Smoothness, ductility and wear resistance makes BALINIT CNI also a powerful alternative to hard chrome plating for textile fibre guiding elements.

  • High oxidation resistance for high temperature applications
  • High ductility, high thicknesses possible
  • High textile fibre wear resistance
  • Alternative to hard chromium plating
BALINIT CNI
Material de recubrimiento CrN
Tecnología de recubrimiento Sputter
Color del recubrimiento gris plata
Dureza recubrimiento HIT [GPa]* 18 +/-3
Coeficiente de fricción (en seco) frente al acero** ~0.5
Temp. máx. de trabajo [°C]**** 700
Temperatura de proceso [°C] < 250
Observaciones generales Todos los datos aportados son valores aproximados, dependen de la aplicación, el entorno y las condiciones de prueba.
*Dureza recubrimiento HIT [GPa] Medido mediante nano indentación de acuerdo con la norma ISO 14577. Para multicapas, la dureza de las diferentes capas varía. La dureza puede adaptarse a la aplicación.
**Coeficiente de fricción (en seco) frente al acero Determinado mediante prueba bola en disco en condiciones secas con una bola de acero de acuerdo con ASTM G99. Durante el rodaje los valores dados pueden superarse.
****Temp. máx. de trabajo [°C] Estos son valores aproximados fuera del campo. Debido a las leyes de la termodinámica existe una dependencia de la presión en la aplicación.