BALINIT® TRITON STAR combines a high hardness with an extremely low coefficient of friction. Being a diamond-like carbon coating (DLC), it provides particularly good protection against abrasive and adhesive wear. The added metal-based support layer (chromium nitride) significantly increases the load-bearing capacity and makes BALINIT® TRITON STAR the coating of choice e.g. for a wide range of popular aluminium forming processes.
| BALINIT TRITON STAR | |
|---|---|
| Materiale di rivestimento | CrN / a-C:H |
| Tecnologia Coating | PACVD |
| Colore del rivestimento | nero |
| Durezza rivestimento HIT [GPa]* | ~15-25 |
| Coefficiente di attrito (asciutto) rispetto all'acciaio** | 0.1 - 0.2 |
| Temp. max. di servizio [°C]**** | 300 |
| Temperature di processo [°C] | < 250 |
| Nota generale | Tutti i dati forniti sono valori approssimativi; dipendono dall'applicazione, dall'ambiente e dalla condizione di test. |
| *Durezza rivestimento HIT [GPa] | Misurato per nanorientro secondo ISO 14577. Per i multistrati la durezza dei diversi strati è variabile. La durezza può essere adattata all'applicazione. |
| **Coefficiente di attrito (asciutto) rispetto all'acciaio | Determinata dal test sfera su disco in condizioni asciutte con una sfera di acciaio secondo ASTM G99. Durante il rodaggio i valori forniti potrebbero essere superati. |
| ****Temp. max. di servizio [°C] | Questi sono valori approssimati esterni dal campo. A causa delle leggi della termodinamica esiste una dipendenza dalla pressione nell'applicazione. |