Turbine Pro
Industrial Gas Turbine
Steam Turbines
Engine in flight

The high hardness and tenacity of BALINIT TURBINE PRO gives outstanding protection against abrasive wear, solid particle erosion and liquid droplet erosion, making it ideal for highly stressed precision components even under high thermal conditions. The finished coated product has extremely low surface roughness (<0.1Raµm) without any post coating machining.

The BALINIT TURBINE PRO family of coatings using a titanium aluminium nitride (TiAlN) structure results in an optimal relation of high hardness to residual compressive stress. This gives great performance especially for highly stressed components.

BALINIT TURBINE PRO can be applied to your steels, super alloys and titanium components with minimal effects to fatigue life.

BALINIT TURBINE PRO
Coating material TiAlN
Coating technology Arc
Coating colour violet-grey
Coating hardness HIT [GPa]* 32 +/- 2
Coefficient of friction (dry) vs. steel** ~0.6
Max. service temp. [°C]**** 700
Process temperature [°C] < 500
Typical coating thickness [µm] 5 - 25
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.