BALINIT DYLYN

Outstanding corrosion protection and anti-adhesion properties, have made BALINIT® DYLYN a well-established coating. Its wear protection and friction properties  are especially important for mechanical engineering, plastics processing and the semiconductor industry.

During the process of Plasma Assisted Chemical Vapour Deposition (PACVD), chemical reaction is caused by plasma excitation and ionization. Optimum quality and performance is ensured by coating in a clean environment under vacuum conditions, and by correct handling of parts and components, a critical task, in which we are highly experienced.

BALINIT® DYLYN is also used for cavities and moulding applications in the medical industry and packaging industries (especially for screw cap and PET bottle manufacturing), as well as for all of the moving and sliding parts of injection moulding tools.

BALINIT DYLYN PRO
Coating material a-C:H:Si
Coating technology PACVD
Coating colour Black
Coating hardness HIT [GPa]* ~ 15-25
Coefficient of friction (dry) vs. steel** 0.05 - 0.2
Max. service temp. [°C]**** 300
Process temperature [°C] < 220
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.
BALINIT DYLYN PLUS
Coating material a-C:H:Si
Coating technology PACVD
Coating colour black
Coating hardness HIT [GPa]* ~17-23
Coefficient of friction (dry) vs. steel** 0.05 - 0.2
Max. service temp. [°C]**** 300
Process temperature [°C] < 220
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.
BALINIT DYLYN
Coating material a-C:H:Si
Coating technology PACVD
Coating colour black
Coating hardness HIT [GPa]* ~ 15-25
Coefficient of friction (dry) vs. steel** 0.05 - 0.2
Max. service temp. [°C]**** 300
Process temperature [°C] < 220
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
**Coefficient of friction (dry) vs. steel Determined by ball-on-disc test in dry condition with an Steel ball according to ASTM G99. During run-in the given values may be exceeded.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.