When the highest part quality is required, together with tool design and geometry, edge preparation and interface engineering, especially tightest tolerances in tool diameter and coating thickness must be ensured to achieve best results.

BALDIA® COMPOSITE DC enables the best possible finishing accuracy through consistently high tool performance with tight bore tolerances when machining carbon fibre (CFRP), glass fibre (GFRP), stack material and aluminium alloys (Si > 12%).

By choosing BALDIA® COMPOSITE DC, you also profit from an enhanced quality control and a special chemical pre-treatment of the substrate.

BALDIA COMPOSITE DC
Coating material C-based (sp3)
Coating technology CVD
Coating colour grey
Coating hardness HIT [GPa]* 80 - 100
Max. service temp. [°C]**** 600
Process temperature [°C] < 900
Typical coating thickness [µm] 4 - 15
General remark All given data are approximate values, they depend on application, environment and test condition.
*Coating hardness HIT [GPa] Measured by nano indentation according to ISO 14577. For multilayers the hardness of the different layers varies. Hardness can be adapted to the application.
****Max. service temp. [°C] These are approximate values out of the field. Due to thermodynamic laws there is a dependency of pressure in application.