BALINIT CNI coated
BALINIT CNI coated for valve
BALINIT CNI coated for piston ring
BALINIT CNI

BALINIT CNI is a very smooth sputtered Chromium Nitride (CrN) coating. It is very ductile and has a high oxidation resistance. It is the coating which can be produced in highest thicknesses (up to 50 µm). Mainly used for high temperature sliding applications like engine exhaust valves and piston rings. Smoothness, ductility and wear resistance makes BALINIT CNI also a powerful alternative to hard chrome plating for textile fibre guiding elements.

  • High oxidation resistance for high temperature applications
  • High ductility, high thicknesses possible
  • High textile fibre wear resistance
  • Alternative to hard chromium plating
BALINIT CNI
Material de recobriment CrN
Tecnologia de recobriment Sputter
Color de recobriment gris platejat
Duresa recobriment HIT [GPa]* 18 +/-3
Coeficient de fregament (sec) vs. acer** ~0.5
Temperatura màx. de treball [ºC]**** 700
Temperatura de procés [°C] < 250
Observació general Totes les dades donades són valors aproximats, depenen de l'aplicació, entorn i condicions de la prova.
*Duresa recobriment HIT [GPa] Mesurat amb nano indentació segons ISO 14577. Per a multicapes, la duresa de les diferents capes varia. La duresa es pot adaptar a l’aplicació.
**Coeficient de fregament (sec) vs. acer Dades determinades mitjançant el test “ball-on-disc” en condicions de sec amb una bola d’acer conforme a ASTM G99. Durant el rodament, les dades donades poden ser superades.
****Temperatura màx. de treball [ºC] Aquests són valors aproximats fora del camp. A causa de la normativa termodinàmica, hi ha dependència de pressió en l'aplicació.